Carbon fiber reinforced polyphenylene sulfide

Carbon fiber reinforced polyphenylene sulfide(PPS) has advantages of electric conduction, high strength, corrosion resistance, high temperature resistance, flame retardant, wear resistance and stable size. It is widely applied in gear, sealing ring, mechanical fittings, robot and etc.
Product data

Item

Testing method

Unit

CF30

Mechanical properties

Tensile strength

ASTM D638-2010

MPa

196

Elongation Elongation at Break

%

/

Flexural Strength

ASTM D796-2010

MPa

284

Flexural Modulus

MPa

26510

Izod  impact  strength(Unnotched)

 

ASTM D256-2010

J/m

367

Izod impact strength(V-notched)

J/m

65

Charpy Impact Strength(Unnotched)

GB/T 1043-2008

KJ/m²

/

Charpy Impact Strength(V-notched)

KJ/m²

/

Thermal properties

Vicat Softening Temperature

GB/T 1634.2-2008

/

Heat Deflection Temp( Tff1.8)

265

Other

Density Density

ASTM  D792

g/cm³

1.46

Hardness

GB/T 2411-2008

HD

/

Melt Mass Flow Rate

GB/T 3682-2000

g/10min

/

Volume Resistivity

ASTM D-257

Ω.cm

≤10³

Water Content

GB/T 5009.3-2003

%

/

Ash content

GB/T 9345-2008

%

31

Mold shrinkage

ASTM D955

%

0.05-0.2

Shooting technique

Drying temperature

(100--110)℃

Drying time

(4--6)h

Injection temperature

(270--310)℃

Mold temperature

(120--140)℃

 